Extraction of Lightweight Platanus orientalis L. Fruit’s Stem Fiber and Determination of Its Mechanical and Physico-Chemical Properties and Potential of Its Use in Composites

Natural fibers extracted from plants are preferred as an alternative to synthetic products. The main reasons for this preference are their affordable cost, light weight and good mechanical properties. However, finding new natural raw materials is challenging due to growth limitations in different geographical areas. Platanus orientalis L. (Eastern plane tree) is a tree with abundant fruits that can grow in many regions of the world. The aim of this study was to determine the mechanical (tensile strength, tensile modulus, elongation), physical (density, fiber diameter) and chemical (cellulose, hemicellulose and lignin) properties of Platanus orientalis L. fruit’s stem by fiber extraction from the stems of the tree. It was determined that the extracted fiber had good mechanical properties and cellulose content of 42.03%. As a result of thermogravimetric analysis, it was determined that the plane tree fruit’s stem fiber had thermal resistance of up to 299 °C. The tensile strength value was 157.76 MPa, the tensile modulus value was 1.39 GPa and the elongation value was 22.01%. It was determined that it is suitable for use in fiber reinforcement in thermoplastic-based composites at temperatures below 299 °C. According to the results obtained by the mechanical, chemical and physical analysis of Platanus orientalis L. fruit’s stem fiber (PoLfs), it could be recommended as a suitable alternative as a reinforcing fiber in thermoplastic and thermoset composites.